Fabrication and characterization of cadmium sulfide nanowires on aluminum oxide template
Loading...
Date
2015
Authors
Journal Title
Journal ISSN
Volume Title
Publisher
UNIVERSITY OF MANAGEMENT AND TECHNOLOGY
Abstract
Cadmium supplied nanowires have unique electrical and optical properties and applications. To obtain cadmium supplied nanowires with regular and good aspect ratio, they can be synthesized by template synthesis method. Porous anodized aluminium oxide is most promising template with regular hexagonal shapes. Their aspect ratio can be controlled by controlling the pores' depth and diameter which greatly depend on anodization voltage and temperature of the electrolyte. In this research, high purity aluminium was used to prepare nanotemplates at 5-6°C in 1M phosphoric acid and cadmium supplied was deposited electrochemically using a co-solution of thiourea, cadmium acetate and ammonium acetate. pH was maintained at 11 in heat bath at 75°C with the help of aqueous ammonia solution. Both porous anodized alumina and cadmium supplied Nanowires were characterized suing SEM. A good quality Nanowires were obtained in bunches with reasonably high aspect ratio.
Description
SUPERVISOR: DR. Sammia Shahid
Keywords
MS Thesis, Cadmium, Nanowires, Aluminum oxide template, Cadmium sulfide nanowires